UPVC工業(yè)化工管材管件
當前位置：首頁 > 產(chǎn)品中心 > UPVC工業(yè)化工管材管件 >
UPVC工業(yè)化工管材管件
產(chǎn)品介紹
| 公稱壓力等級和規(guī)格尺寸 | |||||||
| 公稱外徑dn | S20 | S16 | S12.5 | S10 | S8 | S6.3 | S5 |
| SDR41 | SDR33 | SDR26 | SDR21 | SDR17 | SDR13.6 | SDR11 | |
| 公稱壁厚en | |||||||
| 16 | 2.0 | ||||||
| 20 | 2.0 | ||||||
| 25 | 2.0 | 2.3 | |||||
| 32 | 2.0 | 2.4 | 2.9 | ||||
| 40 | 2.0 | 2.4 | 3.0 | 3.7 | |||
| 50 | 2.0 | 2.4 | 3.0 | 3.7 | 4.6 | ||
| 63 | 2.0 | 2.5 | 3.0 | 3.8 | 4.7 | 5.8 | |
| 75 | 2.3 | 2.9 | 3.6 | 4.5 | 5.6 | 6.8 | |
| 90 | 2.8 | 3.5 | 4.3 | 5.4 | 6.7 | 8.2 | |
| 110 | 3.4 | 4.2 | 5.3 | 6.6 | 8.1 | 10.0 | |
| 125 | 3.9 | 4.8 | 6.0 | 7.4 | 9.2 | 11.4 | |
| 140 | 4.3 | 5.4 | 6.7 | 8.3 | 10.3 | 12.7 | |
| 160 | 4.0 | 4.9 | 6.2 | 7.7 | 9.5 | 11.8 | 14.6 |
| 180 | 4.4 | 5.5 | 6.9 | 8.6 | 10.7 | 13.3 | 16.4 |
| 200 | 4.9 | 6.2 | 7.7 | 9.6 | 11.9 | 14.7 | 18.2 |
| 225 | 5.5 | 6.9 | 8.6 | 10.8 | 13.4 | 16.6 | |
| 250 | 6.2 | 7.7 | 9.6 | 11.9 | 14.8 | 18.4 | |
| 280 | 6.9 | 8.6 | 10.7 | 13.4 | 16.6 | 20.6 | |
| 315 | 7.7 | 9.7 | 12.1 | 15.0 | 18.7 | 23.2 | |
| 355 | 8.7 | 10.9 | 13.6 | 16.9 | 21.1 | 26.1 | |
| 400 | 9.8 | 12.3 | 15.3 | 19.1 | 23.7 | 29.4 | |
| 管材物理性能 | |||
| 項目 | 單位 | 技術(shù)指標 | 試驗方法 |
| 密度 | kg/m³ | 1350-1460 | GB/T 1033-1986方法A |
| 維卡軟化溫度 | ℃ | ≥80 | GB/T 8802-2001 |
| 縱向回縮率 | % | ≤5 | GB/T 6671-2001 |
| 二氯甲烷浸漬試驗 | 15℃，30min | 式樣表面無破壞 | GB/T 13526-1992 |
| 管件物理性能 | |||
| 項目 | 單位 | 技術(shù)指標 | 試驗方法 |
| 密度 | kg/m³ | 1350-1460 | GB/T 1033-1986方法A |
| 維卡軟化溫度 | ℃ | ≥70 | GB/T 8802-2001 |
| 烘箱試驗 | 無脫層，無開裂 | GB/T 8803-2001 | |
| 管材力學性能 | ||||
| 項目 | 試驗參數(shù) | 技術(shù)要求 | ||
| 溫度/℃ | 時間/h | 環(huán)應力/Mpa | ||
| 靜液壓試驗 | 20 | 1 | 40 | 無破裂，無滲漏 |
| 20 | 100 | 34 | ||
| 20 | 1000 | 30 | ||
| 60 | 1000 | 10 | ||
| 落錘沖擊試驗 | 0℃ TIR | ≤10% | ||
| 管件力學性能 | ||||
| 項目 | 試驗參數(shù) | 技術(shù)要求 | ||
| 溫度/℃ | 時間/h | 環(huán)應力/Mpa | ||
| 靜液壓試驗 | 20 | 1 | 40 | 無破裂，無滲漏 |
| 20 | 100 | 34 | ||
| 20 | 1000 | 30 | ||
| 60 | 1000 | 10 | ||
| 墜落試驗 | 0℃ | 無破裂 | ||